The fabrication of chiral nanostructures gives rise to characteristic chiroptical activity, which can be used for chirality‐based biosensors. Great progress is made in the use of nanoassemblies for the construction of chiral nanoparticle dimers, pyramids, helices, and twisted structures, and their chiroptical activities correlate with diverse structural geometries and enantiomeric configurations. In DNA‐hybridization‐based chiral nanoassemblies, the assembly parameters, such as the components, gaps, multicomponents, and the aftergrowth of metal, can result in multiple bands and enhanced chiroptical effects. Based on known chiral nanostructures, the existing chiral nanoassembly‐based biosensors together with their targets and signal amplification strategies are reviewed. Chirality involves multiple signals, and multitarget biosensors are introduced with newly developed chiral architectures for the accurate and reliable monitoring of biomarkers in living cells. The interactions between chiral nanoarchitectures and biosystems are also highlighted, which are important not only in the chiral dynamic switching of nano‐objects for biomonitoring, but also in manipulating cell growth, proliferation, and adhesion. The future perspectives on chiral fabrication and its use in biosensors are also comprehensively discussed.     

18F-NaF注射液的制备及新西兰兔骨折显像

由外伤或肿瘤骨转移造成的隐匿性骨折和愈合情况的准确诊断对制定合适的治疗方案具有非常重要的意义。为考查¹⁸F-NaF PET显像用于骨折诊断的诊断效能，本研究制备了¹⁸F-NaF注射液，并对其进行了质量控制和稳定性研究，然后建立新西兰兔骨折动物模型，模型建立约2周后进行了¹⁸F-NaF PET显像和⁹⁹Tc^m-亚甲基二磷酸盐（⁹⁹Tc^m-MDP）SPECT显像的自身对照实验，并对显像效果进行了比较。结果表明：¹⁸F-NaF的产量大于37 GBq，各项检验结果均符合质控要求，40 ℃下放置8 h和30 ℃下放置10 h所有检验结果均无明显变化；¹⁸F-NaF PET和⁹⁹Tc^m-MDP SPECT两种显像方式均可见全身骨骼，骨折部位呈明显放射性浓聚，但¹⁸F-NaF给药后30 min即可进行PET显像，骨折部位显示更为清晰，骨折部位与对侧正常骨骼的放射性摄取比（T/NT）明显高于⁹⁹Tc^m-MDP，而⁹⁹Tc^m-MDP需在给药后2 h才能进行SPECT显像。本研究表明¹⁸F-NaF PET对骨折的显像性能优于⁹⁹Tc^m-MDP，可明显提高检查流通量和诊断效能。     

Corrosion protection of aluminum alloy by epoxy coatings containing polyaniline modified graphene additives

In the study, polyaniline/reduced‐graphene oxide (PANI‐RGO) composites, fabricated by loading 2, 5, and 8wt% graphene oxide, was prepared by in‐situ emulsion polymerization and reduction. They are characterized by Fourier transform infrared spectroscopy, X‐ray diffraction, and scanning electron microscopy. Epoxy coatings adding PANI and PANI‐RGO composites were coated on the surface of AA5083 Al alloy. The anticorrosion performance of the coatings is measured by electrochemical impedance spectroscopy and potentiodynamic polarization curve in 3.5wt% NaCl solution. The results demonstrate that the epoxy/PANI‐RGO coating exhibits a better protection against AA5083 alloy corrosion compared with the epoxy/PANI coating. Enhancement of the passivation performance of PANI was obtained by the addition of RGO into epoxy/PANI coating system.     

热处理对挤压态Mg-6Gd-5Y-1Zn合金组织与性能的影响

通过对Mg-6Gd-5Y-1Zn(质量分数,%)合金在固溶和时效处理状态下显微组织和力学性能的研究发现,α-Mg基体、沿挤压方向分布的条状18R-LPSO相、少量的Mg₂₄(GdYZn)₅ 相以及细层片状的14H-LPSO相构成了挤压态合金的组成相。挤压态合金经固溶(T4)处理后,一部分18R-LPSO相溶入基体,并且基体中的14H-LPSO相伸长同时粗化。挤压态合金经过固溶加时效(T6)处理后,大量β′相从α-Mg基体中析出。T6态合金的室温力学性能最好,其屈服强度、抗拉强度及伸长率分别为272 MPa、406 MPa和6.1%。β′相沉淀也发生在挤压态合金的直接人工时效(T5)处理过程,但相比于T6处理,14H-LPSO相和β′相在基体中的体积分数均偏低。     

高性能三水醋酸钠-尿素-膨胀石墨混合相变材料的制备及其在电地暖中的应用性能

采用尿素调节三水醋酸钠的相变温度到合适范围再添加膨胀石墨来降低过冷度，研制了高性能的三水醋酸钠-尿素-膨胀石墨混合相变材料，并对其在电地暖中的应用性能进行了研究。结果表明，当尿素质量分数为36.5%、膨胀石墨添加量为4%(质量)时，所得混合相变材料的熔化焓高达209.1 J/g，熔点在31.98℃，过冷度仅为2.04℃，热导率为2.349 W/(m·K)，热可靠性良好；将用该混合相变材料制成的相变板安装在实验房的电地暖中时，实验房的热舒适度随着相变材料层厚度的增加而增加，但也带来加热时间和用电量的增加；当相变材料层厚度为10 mm时，电加热温度适宜设置在45℃；在热舒适度相当的条件下，有相变板的实验房与无相变板的参比房相比具有用电量小及电费低的优势。     